“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.
Export
Đurović, Miraš, 1949-
Uticajni faktor na pojavu površinskih pukotina pri toplom valjanju plemenito-ugljeničnih čelika sa povećanim sadržajem oligoelemenata
Autorstvo-Nekomercijalno-Bez prerade 3.0 Srbija (CC BY-NC-ND 3.0)
Academic metadata
Phd. theses
Tehnicko-tehnološke nauke
doktor nauka - metalurško inženjerstvo
Univerzitet Crne Gore
Metalurško-tehnološki fakultet
Studijski program Metalurgija
Other Theses Metadata
The influential factors surface cracking during hot rolling of plain carbon steels with an increased content of tramp elements
[M. Đurović]
PDF/A (105 listova)
Perović, Boško, 1929- (mentor)
Trajkov, Stevo (član komisije)
Lamut, Jakob (član komisije)
Radulović, Branko, 1950- (član komisije)
Blečić, Žarko, 1952- (član komisije)
Prezentiram rad je posvećen fizičko-metalurškom izućavanju uticaja rezidualnih elemenata kao što su Cu. Sn. Sb i S na površinsku krtost u toplom. plastičnost pri toplom uvijanju i na pojavu određenih defekata pri valjanju kontinuirano livenih gredica niskougljemčnih čehka.Određivana je sklonost ka površinskim pukotinama, deformabilnost i obogaćivanje sloja ispod kovarine i granica austenitnih zrna oligoelementima za vrijeme zagrijavanja niskougljničnog čelika sa povećanim sadržajem Cu (0.18 - 1.11%), Sn (0.040 - 0.105%) i Sb(0 003 - 0.042%) na osnovu ispitivanja toplim savijanjem, toplim uvijanjem i mikroanalize pomoću mikrosonde Prije ispitivanja uzorci čelika su zagrijavani 0 , 5 - 3 sata u peći sa
vazdušnom atmosferom uobičajene i povećane vlažnosti na 900 - 1250°C. Rezultati su pokazali da je površinska krtost u direktnoj vezi sa Cu-obogaćivanjem sloja ispod kovanne i da temperatura zagrijavanja i sadržaj Cu u čeliku imaju presudan uticaj na ove pojave. Sa povišenjem temperature zagrijavanja površinsko Cu-obogaćivanje se povećava, dostiže maksimum na 1100 - 1I50°C, a da sa daljim rastom temperature se smanjuje i postepeno iščeza\>a U radu je analiziran mehanizam ove promjene.Prema rezultatima ispitivanja penetracija tečne Cu-bogate faze duž granica austenitnih zrna dešava za vrijeme zagrijavanja.
Povećan sadržaj kalaja i antimona u čeliku pojačava efekat bakra na obrazovanje pnvršinskih pukotina. Slično Cu. Sn i Sb obogaćuju sloj ispod kovarine i izazivaju proširenje temperaturne oblasti krtosti kako prem a višim, tako i prema nižim temperaturama. Površtnska krtost u toplom i obogaćivanje površinskog sloja sa Cu. Sn i Sb povećavaju se u prisustvu vodenc pare u atmosferi peći, posebno kod čelika sa povećanim sadržajem kalaja u tem peratumom intervalu 1150 — 1250°C. Povećan sadržaj sumpora u čeliku doprinosi smanjenju inteziteta pukotina nastalih pod uticajem povećanog sadržaja bakra. Međutim.visoka aktivnost S ka osnom segregiranju za vrijcme očvršćavanja konti livenih gredica kao i taloženje sitnih sulfida po granicama austenitnih zrna. hmitirajući su faktori za korišćenje ovog povoljnog efekta sumpora.
Ispitivanje makrostrukture konti livenih gredica pokazalo je da pri uslovima kontinuiranog livenja koji doprinose povećanju zone stubastih kristala nastaju izrazite aksijalne segregacije i jače izraženi unutrašnji efekti duž ose gredice. U tom slučaju oligoelementi mogtt da doprinesu nastajanju oslabljenih mjesta duž ose gredice. a time i cijepanju prednjeg kraja valjanog komada pri valjanju. Međutim. uslovi livenja koji favorizuju formiranje šire pothlađene i velike centralne jednakoosne zone. smanjuju osne segregacije i sklonost ka cijepanju prednjeg kraja valjanog komadakao i sk/onost ka površinskim pukotinama pri valjanju.
Ustanovljeno je da obogaćivanje sloja ispod kovarine oligoelementima ne utiču na
deformabilnost pri toplom uvijanju, mada broj uvijanja do loma na visokim temperaturama (1100 - 1200°C) jako zavisi od srednjeg sadržaja oligoelemenata u čeliku, posebno od sadržaja kalaja.
The presented work is devoted to the physical metallurgy study of influence of the residual elements as Cu. Sn. Sb. and S on the surface hot shortness, the deformability during hot torsion and on the appearance some specific defects during hot rolling continuously cast billets of plain carbon steels. The susceptibility to surface cracking, deformability and enrichment of the subscale layer and the austenite grain boundaries with residuals during heating carbon plain steel with an increased content of Cu (0.18 - 1.11%). Sn (0.020-0.105%) and Sb (0.003- 0.042%) were investigated using a bending test, a hot torsion test and electron probe microanalysis. Before testing the steels were heated for 0.5-3 hours in a furnace with an air atmosphere of common and increased wet at 900 - 1250°C. It was found that the surface shortness is directly connected to the Cu-enrichment in the subscale layer and that both the reheating temperature and the copper content of the steel had a crucial influence on these phenomenons With an increase of the reheating temperature the Cu enrichmenl increased too and reached it's maximum value at /100 1150°C After this it decreased and gradually disappeared at a still higher temperatures A mechanism of these changes was discussed The results have shown that the penetration of the liquid Cu-enriched phase along austenite grain boundaries to take place during the heating. The increased tin and antimony content in the steel intensifies the effect of copper on the surface cracks formation. Like Cu. Sn and Sb enrichment sub scale layer and produced a larger temperature shortness area at both higher and lower temperatures. The surface hot shortness and the enrichment subscale layer with Cu. Sn and Sb are increased by the presence of water vapor in furnace air atmosphere, especially of the steels with the increased tin content and h. the temperature range 1100-1250°C. An increased content of sulphur in the steel contributions to reduce the intensity of cracking produced by increased copper content However, the haig axial segregation activity of S during the solidification continuously cast bilets as well as the detrimental precipitation of fine sulphides at austenite grain boundaries, represents some limiting parameters for making use of it's beneficial effect The resting of macrostructure of continuously cast billet was shown that under certain continuous casting condition which favor the columnar mode of growth, the axial segregation of S. P. Sn and Sb and some internal defects along the central axis of the billet becomes severe. In that case the tramp elements accentuated a weakness along the centre line of billet which can lead to problems with formation an "alligatoring type" of fracture of the workpiece front end by rolling. How ever, conditions which favor an increased of chill zone and a large equiaxed zone have been found to reduce the degree of axial segregation and the susceptibility to "alligatoring" type of fracture of the w orkpiece front and as well as the surface cracking during rolling. It was found that a residuals enriched subscale layer cannot affect the workability measured with a hot-torsion test, although the number of revolution to fracture at high temperature (1100-1200C.) depends strongly on the average content of residual in the steel, especially the content of tin.
surface hot shortness, Cu-enrichment, subscale laver, carbon steel, residuals, tramp elements. deformability, bending test, torsion test
Serbian
21504516
Tekst.
Prezentiram rad je posvećen fizičko-metalurškom izućavanju uticaja rezidualnih elemenata kao što su Cu. Sn. Sb i S na površinsku krtost u toplom. plastičnost pri toplom uvijanju i na pojavu određenih defekata pri valjanju kontinuirano livenih gredica niskougljemčnih čehka.Određivana je sklonost ka površinskim pukotinama, deformabilnost i obogaćivanje sloja ispod kovarine i granica austenitnih zrna oligoelementima za vrijeme zagrijavanja niskougljničnog čelika sa povećanim sadržajem Cu (0.18 - 1.11%), Sn (0.040 - 0.105%) i Sb(0 003 - 0.042%) na osnovu ispitivanja toplim savijanjem, toplim uvijanjem i mikroanalize pomoću mikrosonde Prije ispitivanja uzorci čelika su zagrijavani 0 , 5 - 3 sata u peći sa
vazdušnom atmosferom uobičajene i povećane vlažnosti na 900 - 1250°C. Rezultati su pokazali da je površinska krtost u direktnoj vezi sa Cu-obogaćivanjem sloja ispod kovanne i da temperatura zagrijavanja i sadržaj Cu u čeliku imaju presudan uticaj na ove pojave. Sa povišenjem temperature zagrijavanja površinsko Cu-obogaćivanje se povećava, dostiže maksimum na 1100 - 1I50°C, a da sa daljim rastom temperature se smanjuje i postepeno iščeza\>a U radu je analiziran mehanizam ove promjene.Prema rezultatima ispitivanja penetracija tečne Cu-bogate faze duž granica austenitnih zrna dešava za vrijeme zagrijavanja.
Povećan sadržaj kalaja i antimona u čeliku pojačava efekat bakra na obrazovanje pnvršinskih pukotina. Slično Cu. Sn i Sb obogaćuju sloj ispod kovarine i izazivaju proširenje temperaturne oblasti krtosti kako prem a višim, tako i prema nižim temperaturama. Površtnska krtost u toplom i obogaćivanje površinskog sloja sa Cu. Sn i Sb povećavaju se u prisustvu vodenc pare u atmosferi peći, posebno kod čelika sa povećanim sadržajem kalaja u tem peratumom intervalu 1150 — 1250°C. Povećan sadržaj sumpora u čeliku doprinosi smanjenju inteziteta pukotina nastalih pod uticajem povećanog sadržaja bakra. Međutim.visoka aktivnost S ka osnom segregiranju za vrijcme očvršćavanja konti livenih gredica kao i taloženje sitnih sulfida po granicama austenitnih zrna. hmitirajući su faktori za korišćenje ovog povoljnog efekta sumpora.
Ispitivanje makrostrukture konti livenih gredica pokazalo je da pri uslovima kontinuiranog livenja koji doprinose povećanju zone stubastih kristala nastaju izrazite aksijalne segregacije i jače izraženi unutrašnji efekti duž ose gredice. U tom slučaju oligoelementi mogtt da doprinesu nastajanju oslabljenih mjesta duž ose gredice. a time i cijepanju prednjeg kraja valjanog komada pri valjanju. Međutim. uslovi livenja koji favorizuju formiranje šire pothlađene i velike centralne jednakoosne zone. smanjuju osne segregacije i sklonost ka cijepanju prednjeg kraja valjanog komadakao i sk/onost ka površinskim pukotinama pri valjanju.
Ustanovljeno je da obogaćivanje sloja ispod kovarine oligoelementima ne utiču na
deformabilnost pri toplom uvijanju, mada broj uvijanja do loma na visokim temperaturama (1100 - 1200°C) jako zavisi od srednjeg sadržaja oligoelemenata u čeliku, posebno od sadržaja kalaja.