“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.
Export
Jelić, Miloš, 1956-
Istraživanje zaostalih napona u postupcima završne prerade i značaj modela njihove distribucije za izbor osobina metalnih materijala
Autorstvo-Nekomercijalno 3.0 Srbija (CC BY-NC 3.0)
Academic metadata
Doktorska disertacija
Tehnicko-tehnološke nauke
doktor nauka - metalurško inženjerstvo
Univerzitet Crne Gore
Metalurško-tehnološki fakultet
Studijski program Metalurgija
Other Theses Metadata
The investigation of residual stresses in final production processes and the importance of their distribution models on metal properties selection
[M. Jelić]
PDF/A (141 list)
Mišović, Mitar, 1952- (mentor)
Drašković, Dragutin, 1936- (član komisije)
Radonjić, Branislav, 1942- (član komisije)
Jaćimović, Milojica, 1950- (član komisije)
Ćulafić, Zoran, 1952- (član komisije)
U radu su priakazni rezultati istraživanja zaostalih napona kod vučenih čeličnih šipki konstrukcionih čelika i njihovog uticaja na mehaničke karakteristike. Proučavani su uslovi deformacije kod vučenja i povezano nehomogeno plastično tečenje sa nastankom zaostalih napona. Praćeno je ponašanje nastalih napona u fazama naknadne dorade vučenih šipki i proveren uticaj zaostalih napona na mehaničke ososbine.
Plastično tečenje kod vučenja stvara uslove za osnosimetrično naponsko stanje zaostalih napona. Relatvni pokazatelj nehomogenosti je linearan sa promenljivim znakom kod aksijalnog, nelinearan i negativan kod radijalnog tečenja sa maksimumom u osi u oba slučaja.
Izmerene vrednosti na površini metodom rentgenske difrakcije su u intervalu od 260 do 640 MPa za aksijalnu, od -1030 do 150 MPa za radijalnu i od -940 do 300 MPa za obimnu komponentu. Aksijalni naponi određeni metodom diflekcije su u intervalu 300 do 670 MPa.
Postupci naknadne obrade znatno menjaju zaostale napone izazivajući njihovu redistribuciju i smanjenje (mehanička obrada), odnosno uklanjanje (temička obrada - žarenje). Razvijeni modeli elastične linije i redistribucija napona kod postupaka mehaničke obrade, odnosno Zenen-Avramova funkcija kod žarenja omogućavaju da se precizno kvantifikuju i kontrolišu promene zaostalih napona kod tih postupaka. Za to su potrebne polazne vrednosti napona, što je takođe dovoljan podatak za simulaciju efekata narušavanja ravnoteže zaostalih napona na osnovu izvedenih modela distribucije.
Uticaj zaostalih napona na mehaničke osobine je ograničen i kod statičkog i kod dinamičkog dejstva sile. Modeli izvornih i redistribuiranih napona utiču na mehaničke osooine u granicama uticaja opora vijanja.
An investigation on residual stresses in drawn Steel bars and their effects on mechanical properties is presented in this issue. Drawing deformation process has been analvzed in non-homogeneous plastic yielding has been correlated with residual stress formation. The behavior of residual stress when drawn bars are subjected to further production processes has been monitored and the effect on mechanical properties is evaluated.
Plastic yielding in drawing process creates conditions for axi-symmetrical residual stress field. The indicator of non-homogeneity rate is linear with both signs by axial yielding, non-linear and negative by radial yielding, both attainmg the highest values at the axis.
Experimental stress values obtained on bar surface by X-Ray diffraction methods are in following ranges: 2б0 - 640 MPa for axial, (-1030) -150 MPa for radial and (-940) - 300 MPa for hoop stresses, while experimental values for axial stresses by deflection method lie between 300 and 670 MPa.
Further production treatment influences residual stresses significantly causing their redistribution and reduction (machining) or their relaxation (heat treatment - annealmg). Models of bar deflection lines and stress redistribution after machining as well as Zener-Avram function in heat treatment processes make stress evaluation possible and set residual stress change under control. This also enables simulation on the effect of residual stress balance disruption conTorming the above models.
Static and dynamic tests showed that in both cases the influence of residual stresses on mechanical properties is not significant. Genuine bar specimens and ones with redistributed stresses have confirmed that residual stress effects do not exceed annealing effects.
zaostali naponi - komponente - uklanjanje - redistribucija, vučenje čelične šipke, rentgenska difrakcija, metoda diflekcije, mehaničke osobine
U radu su priakazni rezultati istraživanja zaostalih napona kod vučenih čeličnih šipki konstrukcionih čelika i njihovog uticaja na mehaničke karakteristike. Proučavani su uslovi deformacije kod vučenja i povezano nehomogeno plastično tečenje sa nastankom zaostalih napona. Praćeno je ponašanje nastalih napona u fazama naknadne dorade vučenih šipki i proveren uticaj zaostalih napona na mehaničke ososbine.
Plastično tečenje kod vučenja stvara uslove za osnosimetrično naponsko stanje zaostalih napona. Relatvni pokazatelj nehomogenosti je linearan sa promenljivim znakom kod aksijalnog, nelinearan i negativan kod radijalnog tečenja sa maksimumom u osi u oba slučaja.
Izmerene vrednosti na površini metodom rentgenske difrakcije su u intervalu od 260 do 640 MPa za aksijalnu, od -1030 do 150 MPa za radijalnu i od -940 do 300 MPa za obimnu komponentu. Aksijalni naponi određeni metodom diflekcije su u intervalu 300 do 670 MPa.
Postupci naknadne obrade znatno menjaju zaostale napone izazivajući njihovu redistribuciju i smanjenje (mehanička obrada), odnosno uklanjanje (temička obrada - žarenje). Razvijeni modeli elastične linije i redistribucija napona kod postupaka mehaničke obrade, odnosno Zenen-Avramova funkcija kod žarenja omogućavaju da se precizno kvantifikuju i kontrolišu promene zaostalih napona kod tih postupaka. Za to su potrebne polazne vrednosti napona, što je takođe dovoljan podatak za simulaciju efekata narušavanja ravnoteže zaostalih napona na osnovu izvedenih modela distribucije.
Uticaj zaostalih napona na mehaničke osobine je ograničen i kod statičkog i kod dinamičkog dejstva sile. Modeli izvornih i redistribuiranih napona utiču na mehaničke osooine u granicama uticaja opora vijanja.